thin dense chrome plating
Thin Dense Chrome Plating
Metalife Industries Inc.

ISO certification

 

Metalife thin dense chrome may conform to your requirements of many specs including:

ML1964-001
AMS2460
QQ-C-320B
AMS2438D

In accordance with:
ASTM B117
ASTM B487<
ASTM B499
ASTM B504
ASTM B571
ASTM D4060-10
ASTM E384
ASTM F519-10
Corrosion Test

 



thin dense chrome plating



 

ROHS



 

OSHA

INDEPENDENT TESTING
Metalife’s tradition of high quality is backed up by independent testing and the results of those tests.  We hope these results prove informative and helpful in your decision to try a Metalife coating.  Please contact us if you would like a copy of the actual report for the results described below.
COMPLIANCE RESULTS FOR OSHA’S NEW STANDARD FOR HEXAVALENT CHROME
AREA PARAMETER METHODOLOGY DATE MINUTES LPM FLOWRATE TOTAL LITERS RESULTS OSHA PEL LIMIT
Tank Operator Hexavalent Chromium OSHA 215-2 6/4/15 421 2.0 842 .045 μg/m3 5.0 μg/m3
Procedure for RoHS Compliance Test:
Hexavalent chromium was analyzed via boiling water leach procedure outlined in Delphi DX900359. Cadmium and lead were determined via flame atomic absorption. Mercury was determined via cold vapor atomic absorption. Coating weight was determined via weigh-strip-weigh using antimony trioxide inhibited hydrochloric acid.


CLICK HERE TO SEE OUR LATEST COMPLIANCE RESULTS FOR RoHS LIMITS


BEND ADHESION TEST PER ASTM B571-97(2008)E1
LAB METHOD TEST RESULTS
Assured Testing Services
Bend
No evidence of internal delamination or loss of adhesion from basis metal.
SALT SPRAY TESTING PER ASTM B117-11
LAB TEST SAMPLE TEST RESULTS PER HOUR
Assured Testing Services 8620 Steel W/16 rms
50 Hrs. 0% red rust
150 Hrs. 5% red rust present
salt spray test 50 hrs salt spray test 150 hrs

50 hrs

150 hrs

MICROHARDNESS EVALUATION PER ASTM E384
LAB TEST SAMPLE TEST LOAD Knoop
Industrial Testing Laboratory Services, LLC Metal Pin 100(g) 1050 avg.
COEFFICIENT OF FRICTION PER ASTM D1894
LAB TEST SAMPLE CoF Static CoF Dynamic
IMR TEST LAB MLP on MLP 0.14 0.14
MLP on 1018 Steel 0.15 0.15

JOURNAL BEARING TEST & THRUST WASHER WEAR TEST RENSSELAER POLYTECHNIC INSTITUTE
Department of Mechanical, Aerospace, and Nuclear Engineering

Conclusion:
“The overall results for the Metalife coated samples show a considerable increase in PV limit when compared to previous tests run on uncoated samples.  Similar comparisons to uncoated wear tests indicate that the wear rate was reduced significantly when coated with the Metalife system.”

Testing Facilities
Scientific Control Laboratories, Inc.
Engineering Services
3158 S. Kolin Avenue
Chicago, IL 60623-4889
Rensselaer
Dept. of Mechanical,
Aerospace, and Nuclear
Engineering
110 8th Street
Troy, NY 12180-3590

TLS, LLC
635 Alpha Dr.
RIDC Park
Pittsburgh, PA 15238

Assured Testing Services
224 River Rd
Ridgeway, PA 15853

  IMR Test Labs
131 Woodsedge Dr
Lansing, NY 14882